Materyèl komen pou mouri-Distribisyon mwazi

Allaj yo itilize nan mouri-Distribisyon yo se sitou ki pa Peye-alyaj . kòm pou metal FERROUS (asye, fè, elatriye .), yo raman itilize akòz pwoblèm tankou materyèl mwazi {{4} Alloys . Sa ki anba la a se yon entwodiksyon tou kout sou mouri-Distribisyon ki pa Peye-ferrous metal .
(1) Klasifikasyon nan alyaj mouri-jete nonperrous anpeche kontraksyon melanje kontraksyon gratis alyaj plon ----- 0.2-0.3% 0.3-0.4% {{4} seri --0.3-0.5% 0.5-0.7% 0.7-0.9% mouri-jete alyaj alyaj alyaj aliminyòm aliminyòm-kwiv seri aliminyòm-mayetik seri ---0.5-0.7% 0.7-0.9% {{16}%}%}}%} {}} {} {} {} {}% {}}% {} {} {}% {} {} {} {}% {}} {} {} {} {} {} {} {} {} {} {{}}% {} {}% {} {}% {} {}% {}% {} {} {{ alloy---------- 0.5-0.7% 0.7-0.9% 0.9-1.1% Copper alloy (2) Recommended casting temperature for various die-casting alloys Alloy type Average wall thickness of casting<=3mm Average wall thickness of casting > 3mm Simple structure Complex structure Simple structure Complex structure
Aliminyòm alyaj aliminyòm silisyòm sistèm 610-650 degre 640-680 degre 600-620 degre 610-650 degre
Sistèm Copper aliminyòm 630-660 degre 660-700 degre 600-640 degre 630-660 degre
Sistèm aliminyòm Mayezyòm 640-680 degre 660-700 degre 640-670 degre 650-690 degre
Aliminyòm Zenk Sistèm 590-620 degre 620-660 degre 580-620 degre 600-650 degre
Zenk alyaj 420-440 degre 430-450 degre 400-420 degre 420-440 degre
Manyezyòm alyaj 640-680 degre 660-700 degre 640-670 degre 650-690 degre
Copper alyaj kwiv òdinè 910-930 degre 940-980 degre 900-930 degre 900-950 degre
Silisyòm kwiv 900-920 degre 930-970 degre 910-940 degre 910-940 degre
* Remak: ① Tanperati a Distribisyon se jeneralman mezire pa tanperati a nan metal la fonn nan gwo founo dife a kenbe .
② Tanperati a Distribisyon nan alyaj zenk pa ka depase 450 degre pou fè pou evite grenn koryas .